What Is Limestone? Building Material.

What Is Lime?

It is an important binding material used in building construction. Lime has been used as the material for construction since ancient times. When it is mixed with sand it provides lime mortar and when mixed with sand and coarse aggregate, it forms lime concrete.

limestone

 Types of Limes and their Properties

The limes are classified as fat lime, hydraulic lime and poor lime:

(i) Fat lime:

It is composed of 95 per cent of calcium oxide. When water is added, it slakes vigorously and its volume increases to 2 to 2.5 times. It is white in colour. Its properties are:

(a) hardens slowly

(b) has a high degree of plasticity

(c) sets slowly in the presence of air

(d) white in colour

(e) slakes vigorously.

(ii) Hydraulic lime:

It contains clay and ferrous oxide. Depending upon the percentage of clay present, the hydraulic lime is divided into the following three types:

(a) Feebly hydraulic lime (5 to 10% clay content)

(b) Moderately hydraulic lime (11 to 20% clay content)

(c) Eminently hydraulic lime (21 to 30% clay content)

lime stone

The properties of hydraulic limes are:

  • Sets underwater
  • The Colour is not perfectly white
  • Forms a thin paste with water and does not dissolve in water.
  • Its binding property improves if its fine powder is mixed with sand and kept in the form of a heap for a week, before use.

 

(iii) Poor lime:

It contains more than 30% clay. Its colour is muddy. It has poor binding property. The mortar made with such lime is used for inferior works.

IS 712-1973 classifies lime as class A, B, C, D and E.

Class A Lime: It is predominantly hydraulic lime. It is normally supplied as hydrated lime and is commonly used for structural works.

 Class B Lime: It contains both hydraulic lime and fat lime. It is supplied as hydrated lime or as quick lime. It is used for making mortar for masonry works.

 Class C Lime: It is predominantly fat lime, supplied both as quick lime and fat lime. It is used for finishing coats in plastering and for whitewashing.

 Class D Lime: This lime contains a large quantity of magnesium oxide and is similar to fat lime. This is also commonly used for whitewashing and for finishing coat in plastering.

 Class E Lime: It is an impure limestone, known as kankar. It is available in modular and block forms. It is supplied as hydrated lime. It is commonly used for masonry mortar.

 

 Tests on Limestones

The following practice tests are made on limestones to determine their suitability:

(i) Physical tests

(ii) Heat test

(iii) Chemical test

(iv) Ball test.

 

(i) Physical Test: Pure limestone is white in colour. Hydraulic limestones are bluish grey, brown or are having dark colours. The hydraulic lime gives out an earthy smell. They are having a clayey taste. The presence of lumps gives an indication of quick lime and unburnt limestones.

 

(ii) Heat Test: A piece of dry stone weighing W1 is heated in an open fire for a few hours. If the weight of the sample after cooling is W2, the loss of weight is W2 – W1. The loss of weight indicates the amount of carbon dioxide. From this, the amount of calcium carbonate in limestone can be worked out.

 

(iii) Chemical Test: A teaspoon full of lime is placed in a test tube and dilute hydrochloric acid is poured into it. The content is stirred and the test tube is kept in the stand for 24 hours. Vigorous effervescence and less residue indicate pure limestone. If effervescence is less and the residue is more it indicates impure limestone.

 

If the thick gel is formed and after test tube is held upside down it is possible to identify a class of lime as indicated below:

  • Class A lime, if the gel does not flow.
  • Class B lime, if gel tends to flow down.
  • Class C lime, if there is no gel formation.

 

(iv) Ball Test: This test is conducted to identify whether the lime belongs to class C or to class B. By adding sufficient water about 40 mm size lime balls are made and they are left undisturbed for six hours. Then the balls are placed in a basin of water. If within minutes slow expansion and slow disintegration start it indicates class C lime. If there is little or no expansion, but only cracks appear it belongs to class B lime. 

 

responsibilitiesESTIMATE AND COASTINGTYPE OF FOUNDATIONtutorials tips

Uses of Lime

The following are the uses of lime in civil works:

(i) For whitewashing.

(ii) For making mortar for masonry works and plastering.

(iii) To produce lime sand bricks.

(iv) For soil stabilisation.

(v) As a refractory material for lining open-hearth furnaces.

(vi) For making cement.

 

 

Benefits of warehouse warehouse storage System

 

 

 

deck sheet DECKING SHEET

 

 

 

 

 

 

 

 

 

Visit our TTC Channel for more information.